Epoxy resin-based, two component, reaction-dry epoxy primer which contains micaceous iron oxide. It prevents corrosion significantly by creating a barrier on the applied surfaces. Due to the miox pigment inside, it can also be used without applying a top coat.

Surface Preparation&Application
Surfaces should be cleaned of old paint film, oil, dust, dirt, moist, chloride, sulphate salts, rust, rolled mud, tempering, casting - welding burrs etc. which will reduce adhesion on the application surface . Bevel the 90° sharp corners and edges of the application surface and send the surface at minimum Sa2 ½ (ISO 8501-1, SSPC-SP10) degrees, (sand - grid scraper) and prime the scraped surface in 1 to 2 hours with Epoxy Shop Primer. After the primer has fully dried (in 4 to 6 hours), Epoxy Miox Barrier Primer can be applied. Mix the barrier and the hardener in the given ratio until a homogeneous mixture is obtained. Rest the mixture for 2 to 3 minutes for preliminary reaction and apply with the recommended apparatuses. The surface temperature must be minimum 3 Celsius degrees higher than the dew temperature. Application at temperatures near the dew point is not recommended. For the topcoat application wait for 24 hours between coats. Application Temperature: Min. +10°C / Max. + 30 °C

Thinning / Blending Ratio
7A / 1B - Epoxy thinner 5- 10% by weight

Coverage Area
4-5 m²/L or 2-3 m²/kg (60 - -80 µ KFK)

Drying Time
Touch dry in 2-3 hours and hard dry in 24 hours.

Recommended Application Tools
Air - airless spray

Package
20 kg Set (17.5 kg A + 2.5 kg B)

Related Products
Corrox 1K Epoxy Primer VIEW DETAIL
Hipox Anti-corrosive Primer VIEW DETAIL
Epoxy Anti-Corrosive Primer VIEW DETAIL
Epoxy Zinc 80 Primer VIEW DETAIL

Sitemizin işlemesini sağlamak için çerezler kullanılmaktadır. Detaylı bilgi almak için Polisan Kansai Çerez Aydınlatma Metni'ni incelemenizi rica ederiz.