Acrylic resin-based, two-component, reaction-dried, aliphatic isocyanate hardener-cured, high-UV-resistant, ultra-gloss, chemical resistant finishing varnish. Highly resistant to yellowing and highly resistant to scratches and impacts.

Surface Preparation&Application
Remove stains, rust, grease and loose paint / coating layer from the application surface, roughen the surface sand the surface. Burn knots without damaging the wood, and remove any resin bleed from the wood. Wipe with Polisel Cellulosic Thinner. Raw wooden surfaces with completed primary surface preparation can be implemented on any kind of massive and wooden surfaces which are treated with Polyester Filling varnish or Polyurethane filling varnish, and grinded. Sandblast the prepared metal surfaces to a minimum degree of Sa2, or ideally to Sa2 ½, and apply epoxy anti-corrosive primer within the following 6 hours. Monitor the dew point during application and avoid treating moist or wet surfaces. Moist and/or water may cause the product to bubble abnormally, become dull or detach from the surface.

Thinning / Blending Ratio
3 pieces Pur-Acryl Varnish, 1 piece Pur-Acryl Varnish Hardener

Coverage Area
10-12 m²/L (varnish+hardener/30-40 micron dry film thickness)

Drying Time
(at 23°C and 50% relative humidity) Dries in 2-3 hours, Time to wait for second coat: At least 24 hours time to become chemically resistant: 7 days.

Recommended Application Tools
Apply with a conventional air spray gun with air pressure: 3-4 bar, nozzle diameter 1.0-1.2 mm and an airless spray gun, and brush for smaller areas.

Package
20 kg Set (15 kg A + 5 kg B)